Influence of the Duration and Temperature of the Al-Fin Process for the Cast Iron Insert on the Microstructure of the Bimetallic Joint Obtained in the Piston Casting Process

Abstract

The aim of this work was to determine the effect of the duration and temperature of the Al-Fin process for casting the bimetallic joint on the formation of the metallurgical bond between the AlSi9 aluminium alloy piston and the cast iron insert. Knowledge about the formation of individual bonding layers has a direct impact on the bonding strength between the aluminium alloy and the EN-GJLA-XNiCuCr15-6-2 austenitic cast iron ring. In the performed tests, the Al-Fin casting process was carried out for different temperatures of the liquid AlSi9 alloy. The temperature of the AlSi9 aluminium alloy varied in the range 700–950 °C in steps of 50 °C. The duration of the Al-Fin process ranged from 1 to 10 min. An optical microscope and a scanning electron microscope were used to study the microstructure of the bimetallic joints. The analysis of the microstructure of the bimetallic bond showed that characteristic layers are formed between the aluminium alloy piston and the cast iron insert: a transition layer, in which iron and aluminium atoms from both joined materials are mixed, and a diffusion layer, in which aluminium and silicon atoms penetrate the surface layer of the joined metals. The thickness of the intermetallic diffusion layer formed between the aluminium alloy and the cast iron insert is thinner and does not depend on the heating time of the aluminium insert in the bath. However, there is a significant effect of both the annealing time and the temperature of the AlSi9 aluminium alloy on the thickness of the transition zone.

Keywords

• bimetallic joint
• cast iron
• microhardness
• microstructure