Effect of yttrium(Y) on structural, morphological and transport properties of CdO thin films prepared by spray pyrolysis technique

Abstract

Cadmium oxide (CdO) and yttrium (Y) doped CdO (Y: CdO) thin films have been prepared onto glass substrate at temperature 300 °C by spray pyrolysis technique. The effects of yttrium (Y) doping on the structural, morphology, optical and electrical properties were studied systematically. The X-ray diffraction (XRD) study confirms that CdO films are polycrystalline in nature with cubic structure having lattice parameter of 0.4658 nm. Surface topographic and nano-structural analysis indicates cluster grain size and porosity decreased substantially with increase of yttrium (Y) content in CdO films. The optical transmittance exhibits excellent optical transparency, with an average transmittance of >70% in the visible range for 2 to 4% yttrium (Y) doping. The optical band gap widens in Y: CdO film from 2.24 to 2.62 eV through Burstein- Moss shift. Hall measurement confirms that material is of n type with a minimum resistivity of 4.7 × 10−4 Ω-cm with carrier concentration of 4.2 × 1021 cm−3 were achieved for 2% yttrium (Y) doping.

Keywords

• Materials science