Boletín de la Sociedad Española de Cerámica y Vidrio (Dec 1999)
Transport properties of doped BICUVOX ceramics
Abstract
Polycrystalline Bi2-xLaxV0.90Cu0.10O5.5-δ (x = 0, 0.10 and 0.20) and Bi1.90Pr0.10V0.90Cu0.10O5.5-δ were prepared by the standard ceramic- synthesis technique. The total electrical conductivity of Bi1.90La0.10V0.90Cu0.10O5.5-δ at temperatures above 500 K is slightly lower than undoped BICUVOX.10, but transport properties in the temperature range 370 - 450 K are similar. Doping BICUVOX. 10 with praseodymium led to the formation of impurity phases, and to both lower conductivity and thermal expansion of ceramic samples. Oxygen-ion transference numbers of phases with moderate rare-earth dopant content (x ≤ 0.10) vary in the range 0.90 - 0.99 at 780 - 910 K and decrease with increasing temperature. Thermal expansion coefficients calculated from the dilatometric data for Bi2-xLnxV0.90Cu0.10O5.5-δ ceramics are (16.1 - 18.0) x 10-6 K-1 at 730 - 1050 K.<br><br>Bi2-xLaxV0.90Cu0.10O5.5-δ (x = 0, 0.10 and 0.20) y Bi1.90Pr0.10V0.90Cu0.10O5.5-δ policristalinos fueron preparados por síntesis cerámica convencional. La conductividad eléctrica total de Bi2-xLaxV0.90Cu0.10O5.5-δ a temperaturas superiores a 500K es ligeramente menor que la correspondiente a BICUVOX.10 no dopada, pero las propiedades de transporte en el rango de temperaturas 370- 450K son similares. Dopando BICUVOX.10 con praseodimio produce la formación de fases secundarias y la reducción de la conductividad y la expansión térmica de las muestras cerámicas. El número de transporte del ión sin oxígeno de fases con un contenido en tierra rara moderado como dopante (x ≤ 0.10) varía en el rango 0.90-0.99 a 780-910k y disminuye con el aumento de la temperatura. Los coeficientes de expansión térmicos calculados a partir de los datos dilatométricos para cerámicas Bi2-xLnxV0.90Cu0.10O5.5-δ son (16.1 - 18.0) x 10-6 K-1 a 730 - 1050 K.