Experimental Study on Subgrade Material of Calcium Silicate Slag

Abstract

Calcium silicate slag (CSS) is used as a secondary solid waste produced by aluminum extraction technology from high alumina fly ash, and its resource utilization has always been a key issue to be solved. In this study, CSS was used to replace a portion of fly ash (FA) to prepare a new inorganic binder stabilized material for road base. The unconfined compressive strength (UCS), phase composition, microstructure, durability and performance index of the base of the test section of the CSS pavement base material were studied. The results showed that with the increase in CSS content, the UCS of pavement base materials gradually increased. Under standard curing conditions, the UCS increased 6.90~17.24% after 7 days, and 7.90~28.95% after 28 days. The main reason was that as the hydration time increased from 7 d to 28 d, the hydration products C-A-S-H gel and C-S-H gel increased, the [SiO4] polymerization degree increased, the crystal type changed, and the structure denser, which supported the good development of mechanical strength of CSS pavement base material. In addition, the research has been successfully applied to a pilot test in Hohhot, China. The freeze–thaw resistance, water stability and UCS of the CSS pavement base material were tested to meet the requirements of Chinese road construction standards, indicating that the application of CSS in pavement base is feasible.

Keywords

• calcium silicate slag
• inorganic binding stable materials
• pavement base
• micromorphology