Effects of external staining on mechanical, optical, and biocompatibility properties of additively manufactured 3Y-TZP ceramic for dental applications

Abstract

Three mole percent yttria-stabilized tetragonal zirconia polycrystal (3Y-TZP) ceramics are exemplary materials for dental restoration due to their high mechanical strength, fracture toughness, chemical endurance, and biocompatibility. Nevertheless, 3Y-TZP ceramics are opaque and their CAD/CAM manufacturing process may cause micro-cracks in conventional clinical practice. In this study, 3Y-TZP ceramic samples were prepared using vat photopolymerization, pre-sintering, external staining, and final high-temperature sintering. The microstructures, mechanical properties, optical properties, and cytotoxicity of the 3Y-TZP ceramic samples were investigated. The results indicate that with increasing Fe3+ concentration of staining solution from 0.1 mol/L to 0.3 mol/L and increasing staining time from 5 s to 30 min, the 3Y-TZP ceramic samples showed a tetragonal crystal structure of zirconia with densely packed grains and a slight increase in grain size. The flexural strength, Vickers hardness, and fracture toughness of 3Y-TZP ceramic samples stained in 0.1–0.3 mol/L Fe3+ solution for 5 s to 3 min were all greater than 665 MPa, 11.9 GPa, and 5 MPa m1/2, respectively, meeting the mechanical requirements for clinical application. Colorimetric analysis revealed a decrease in L* (black-white index) from 90.4 to 81.3, an increase in a* (green-red index) from −1.5 to 3.2, and an increase in b* (blue-yellow index) from 11.6 to 20.3, approximating the commercial VITA 3D-Master Shade Guide chromaticity. Furthermore, the 3Y-TZP ceramic samples exhibited a cell viability of 90% or higher toward L929 cells.

Keywords

• Additive manufacturing
• Optical property
• Staining
• Zirconia ceramic