Materials (Jan 2024)
Investigation into the Acoustic Properties of Polylactic Acid Sound-Absorbing Panels Manufactured by 3D Printing Technology: The Influence of Nozzle Diameters and Internal Configurations
Abstract
Sound-absorbing panels are widely used in the acoustic design of aircraft parts, buildings and vehicles as well as in sound insulation and absorption in areas with heavy traffic. This paper studied the acoustic properties of sound-absorbing panels manufactured with three nozzle diameters (0.4 mm, 0.6 mm and 0.8 mm) by 3D printing from three types of polylactic acid filaments (Grey Tough PLA; Black PLA Pro; Natural PLA) and with six internal configurations with labyrinthine zigzag channels (Z1 and Z2). The absorption coefficient of the sample with the Z2 pattern, a 5.33 mm height, a 0.6 mm nozzle diameter and with Black PLA Pro showed the maximum value (α = 0.93) for the nozzle diameter of 0.6 mm. Next in position were the three samples with the Z1 pattern (4 mm height) made from all three materials used and printed with a nozzle diameter of 0.4 mm with a sound absorption coefficient value (α = 0.91) at 500 Hz. The highest value of the sound transmission loss (56 dB) was found for the sample printed with a nozzle size of 0.8 mm with the Z2 pattern (8 mm height) and with Black PLA Pro. The extruded material, the nozzle diameter and the internal configuration had a significant impact on the acoustic performance of the 3D-printed samples.
Keywords