Growth and Characterisation of Layered (BA)₂CsAgBiBr₇ Double Perovskite Single Crystals for Application in Radiation Sensing

Abstract

A recent publication on single crystals of two-dimensional, layered organic–inorganic (BA)2CsAgBiBr7 double perovskite (BA+ = CH3CH23NH3+) suggested the great potential of this semiconductor material in the detection of X-ray radiation. Our powder XRD measurement confirms the crystallinity and purity of all samples that crystallise in the monoclinic space group P21/m, while the single crystal XRD measurements reveal the dominant {001} lattice planes. The structure–property relationship is reflected in the lower resistivity values determined from the van der Pauw measurements (1.65–9.16 × 1010 Ωcm) compared to those determined from the IV measurements (4.19 × 1011–2.67 × 1012 Ωcm). The density of trap states and charge-carrier mobilities, which are determined from the IV measurements, are 1.12–1.76 × 1011 cm–3 and 10−5–10−4 cm2V–1s–1, respectively. The X-ray photoresponse measurements indicate that the (BA)2CsAgBiBr7 samples synthesised in this study satisfy the requirements for radiation sensors. Further advances in crystal growth are required to reduce the density of defects and improve the performance of single crystals.

Keywords

• single crystals
• (BA)₂CsAgBiBr₇
• two-dimensional organic–inorganic double perovskite
• radiation sensor