Pressureless sintering kinetics analysis of Ti3SiC2 and Ti2AlC powdered MAX phases

Abstract

Abstract This paper reports the pressureless sintering behavior and the activation energy of the powdered MAX phases Ti3SiC2 and Ti2AlC. A non-isothermal technique was used to determine the sintering kinetic parameter. The Ti3SiC2 and Ti2AlC MAX phases showed the maximum sintering rate at 1723 K, 0.14 and 0.10 µm/s, respectively. The sintering rate of the sample at different temperatures followed a cubic equation which was determined. The sintering activation energy (Ea) for the Ti3SiC2 and Ti2AlC samples was 362.1 kJ/mol and 640.3 kJ/mol, respectively.

Keywords

• Ceramic
• Ti3SiC2
• Ti2AlC
• Sintering
• Kinetics parameters