About the Memory of Transformation-Induced Plasticity in 35NCD16 Carbon Steel Subjected to Various Thermomechanical Histories

Abstract

This study deals with Transformation-Induced Plasticity (TRIP) observed in the martensitic transformation of 35NCD16 ferritic steel. In this study, TRIP tests were carried out for two different cases: First, after only free dilatometric (FD) tests, which is used as the reference test for the considered applied stress; second, with TRIP tests being performed similarly to the first case (same thermal cycle, same applied stress) but with pre-thermomechanical loading histories applied. Such histories may be FD tests, TRIP tests, elastoplastic history, etc. The comparison between the results of TRIP test (a) and TRIP test (b) indicates if TRIP holds the memory of the applied loading histories. The current obtained results tell us that TRIP does not hold any significant memory. During the martensite → austenite transformation, the material may present recovery from strain hardening. Waiting for more details about the physical phenomena responsible for the absence of TRIP memory, one can point out the importance of this result as it enables one to use the same specimen for several TRIP tests. However, this result must be validated using other combinations of loading histories (such as multiaxial and cyclic, among others).

Keywords

• TRIP (transformation-induced plasticity)
• FD (free dilatometric) test
• martensite
• austenite
• elastoplasticity
• 35NCD16 ferritic steel