Processing and Application of Ceramics (Dec 2008)
Influence of nitrogen on the tribological properties of a-C:H layers on the polycarbonate substrates
Abstract
Polycarbonate (PC) possesses many commercial applications. However, PC is still limited to non-abrasive and chemical-free environments due to its low hardness, low scratching resistance and high susceptibility to chemical attacks. To overcome this limitation, PC can be coated by hydrogenated amorphous carbon layers. The a-C:H layers have very attractive properties such as high hardness, infrared transparency, chemical inertness, low friction coefficients, and biocompatibility. Addition of nitrogen in the structure allows lowering internal stress and improve tribological properties of a-C:H layers. In this work, a-C:N:H layers were deposited from mixture CH4/N2 gases by RF PECVD method. Effects of the nitrogen incorporation on structure and tribological properties of deposited layers were investigated. The structure of layers were characterized by Fourier Transform Infrared spectroscopy (FTIR) and X-ray photoelectron spectroscopy (XPS). The friction coefficient, wear resistance of a-C:H:N layers were estimated by tribometer in ball-on-disc configuration. The IR spectra of the obtained layers have demonstrated a presence of nitrogen bonded both to carbon and to hydrogen. A formation of the following bonds has been confirmed: -C≡N, -NH2, -C−NH2, >C=NH. They are all typical for a-C:N:H layers. The tribological tests have shown that the layers reduce the friction coefficient of the polycarbonate (up to 50 %) and considerably improve wear resistance.