Design of silver-zinc-nickel spinel-ferrite mesoporous silica as a powerful and simply separable adsorbent for some textile dye removal

Abstract

Abstract Silver-zinc-nickel spinel ferrite was prepared by the co-precipitation procedure with the precise composition Ag0.1Zn0.4Ni0.5Fe2O4 for bolstering pollutant removal effectiveness while upholding magnetic properties and then coated with a mesoporous silica layer. The surface characteristics and composition of Ag0.1Zn0.4Ni0.5Fe2O4@mSiO2 were confirmed using EDX, FT-IR, VSM, XRD, TEM, SEM, and BET methods. The surface modification of Ag-Zn-Ni ferrite with a silica layer improves the texture properties, where the specific surface area and average pore size of the spinel ferrite rose to 180 m2/g and 3.15 nm, respectively. The prepared spinel ferrite@mSiO2 has been utilized as an efficient adsorbent for eliminating methyl green (MG) and indigo carmine (IC) as models of cationic and anionic dyes from wastewater, respectively. Studying pH, Pzc, adsorbent dosage, dye concentration, and temperature showed that efficient removal of MG was carried out in alkaline media (pH = 12), while the acid medium (pH = 2) was effective for IC removal. Langmuir isotherm and pseudo-second-order kinetics were found to be good fits for the adsorption data. Both dyes were adsorbed in a spontaneous, endothermic process. A possible mechanism for dye removal has been proposed. The adsorbent was effectively recovered and reused.

Keywords

• Spinel ferrite@SiO2
• Cationic and anionic dyes
• Adsorption
• Wastewater treatment