Chemical and morphological characterization of <em>Agave angustifolia</em> bagasse fibers

Abstract

The main aim of this study was to characterize cooked bagasse fibers from Agave angustifolia Haw. The fibers were characterized using scanning electron microscopy, differential scanning calorimetry, thermogravimetric analysis, X-ray Diffraction and chemical analysis. The tensile strength was also tested using fibers with a uniform length (30 mm). The fibers were light brown in color, with a mean diameter and length of 501 ?m and 144 mm, respectively. Scanning electron microscopy images revealed elliptically shaped cells with varying lumen size. Holocellulose content was approximately 82.12 %, and total lignin content was approximately 20.69 %. Due to the crystallinity and lignin content, the fibers proved to be thermo-stable until 220 °C. The mean values of tensile strength, Young’s modulus, % strain (?), and ultimate tensile strength were determined via mechanical tests. The results are comparable to those of other common lignocellulosic fibers, confirming their potential use as a reinforcing element in a polymer matrix to form a new biodegradable composite.

Keywords

• chemical composition
• crystallinity
• mechanical tests
• morphology
• thermal analysis