Effects of Passivation with Cu and W on the Corrosion Properties of Super Duplex Stainless Steel PRE 42

Abstract

Carbon steel is subjected to several pretreatments to enable its use in highly corrosive environments, such as marine structures. However, its surface treatment is problematic owing to various processes, and these problems can be solved by replacing it with super duplex stainless steel (SDSS), which exhibits remarkable strength and corrosion resistance owing to its austenite and ferrite phases. EN 1.4410 and EN 1.4501 are the most extensively used SDSS grades in marine structures, as they exhibit exceptional strength and corrosion resistance in seawater. This study subjected EN 1.4410 and EN 1.4501 samples to specific heat treatment after casting and observed their structural alterations through field emission scanning electron microscopy. Their passivation states, with or without the Cu and W layers, were determined by examining their corrosion properties through open-circuit potential measurements, electrostatic polarisation tests, electrochemical impedance spectroscopy (EIS), and critical pitting temperature (CPT) analysis. The inclusion of Cu significantly improved the uniform corrosion resistance within the passivation layers, whereas the addition of W enhanced the pitting resistance (Epit, CPT). Additionally, the EIS analysis confirmed a double-layer structure in the passivation layer of EN 1.4501. Moreover, Cu did not act as a strengthening element of the passivation layer, whereas W significantly reinforced it.

Keywords

• high corrosion steel
• solution annealing
• super duplex stainless steel
• effect of Cu and W
• passivation layer
• corrosion properties