The growth of ruby single crystals

Abstract

Ruby (Cr:Al2O3) single crystals were grown by the Czochralski technique in an argon atmosphere. The critical crystal diameter dc = 1.0 cm and the critical rate of rotation ωc = 20 rpm were calculated by equations of the hydrodynamics of the melt. The rate of crystal growth was experimentally obtained to be 2.7 mm/h. For chemical polishing, conc. H3PO4 at 593 K for an exposure of 3 hours was determined. Conc. H3PO4 at 523 K for an exposure of 3 h was found to be a suitable etching solution. The lattice parameters a = 0.47627(6) nm and c = 1.301(1) nm were determined by X-ray powder diffraction. The obtained results are discussed and compared with published data.

Keywords

• czochralski technique
• ruby
• growth
• single crystal
• etching