Preparation and corrosion resistance properties of duplex stainless steel (00Cr22Ni6MnMoCu)

Abstract

In the present paper, a new kind of duplex stainless steel (DSS, 00Cr22Ni6MnMoCu) was prepared. Cr30 was chosen as a comparison of microstructures and mechanical properties with 00Cr22Ni6MnMoCu. Corrosion tests with 3.5% NaCl solution and electrolytic solution for 00Cr22Ni6MnMoCu were carried out to analyze the corrosion pattern of test materials. It can be concluded that: (1) Austenitic and ferrite duplex stainless steel has an optimized phase distribution, high toughness and strength when the ratio of two-phase content is 1:1. (2) Corrosion tests show that the corrosion resistance of 00Cr22Ni6MnMoCu is 12 times compared to ferrite stainless steel Cr30. (3) Electrolytic corrosion tests show that for 00Cr22Ni6MnMoCu, the corrosion is caused by intergranular corrosion. For Cr30, it is mainly caused by pinholes. However, Cr30 has a poor corrosion resistance because of the presence of a large amount of carbides and their phase boundaries caused by the electric potential difference between the carbide and the matrix.

Keywords

• duplex stainless steel (DSS)
• ferrite stainless steel
• intergranular corrosion
• pinholes corrosion
• solution treatment