Characteristics for Gallium-Based Liquid Alloys of Low Melting Temperature

Abstract

Gallium alloys are ideal base carriers for temperature-sensitive ferrofluids, which can be used for energy convection, soft robotics, microchannels, magnetorheological devices, etc. In this study, gallium was mixed with different substances (In, Sn, Zn, Ge, and Al) to obtain a low melting point, reduce the wetness and adhesion of its alloys, and realize low viscosity. The melting point, contact angle on certain solid plates, viscosity, and viscoelasticity of the gallium alloys were measured, and some useful gallium alloys were obtained. The experimental results showed that Ga80In10Sn10 had lower wettability at a larger contact angle of 148.6° on the Teflon plate. Here, (Ga80In10Sn10)97Zn3 with a melting point of 8.2 °C, lower than the melting point of Galinstan, was developed. It had a viscosity about three times that of water at room temperature and an elastic response from 0.1 to 100 Hz at a 1% strain amplitude for the viscoelasticity. It was expected that a kind of temperature-sensitive magnetic fluid with a gallium-based liquid alloy as the base carrier liquid would be prepared in the future with Teflon as the container to achieve energy conversion under the drive of the magnetic field.

Keywords

• Ga alloy
• melting point
• viscoelasticity
• wetness
• eutectic
• Galinstan