Enhanced Selenate Removal in Aqueous Phase by Copper-Coated Activated Carbon

Abstract

In this study, we prepared a novel sorbent derived from precipitating copper ion onto the surfaces of activated carbon (Cu-AC). The sorbents were comprehensively characterized by Brunauer−Emmett−Teller (BET), zeta potential analysis, SEM, XRD, and FTIR. Batch experiments were conducted to evaluate selenate removal by Cu-AC under different conditions. The results showed that Cu was uniformly coated on the AC surface. Copper pretreatment markedly decreased the specific surface area and total pore volume of AC, and changed its surface zeta potential from highly negative to low negative and even positive. The Cu-AC substantially improved selenate adsorption capacity from the 1.36 mg Se/g AC of raw AC to 3.32, 3.56, 4.23, and 4.48 mg Se/g AC after loading of 0.1, 0.5, 1.0, and 5 mmol Cu/g AC, respectively. The results of toxicity leaching test showed AC coated with ≤1.0 mmol Cu/g was acceptable for potential application. Selenate adsorption was significantly inhibited by high ionic strength (>50 mM NaCl) and pH (>10). The electrostatic attraction between positive surface charge of Cu-AC and selenate ions and hydrogen bonding between CuO and HSeO4− might contribute to selenate sorption. Evidence showed that the selenate adsorption might involve outer-sphere surface complexation. The adsorption data appeared to be better described by Langmuir than Freundlich isotherm. The spent adsorbent could be effectively regenerated by hydroxide for reuse. Only a little decrease of removal efficiency was observed in the second and third run. This study implies that Cu-coated AC is a potential adsorbent for sustainable removal selenate from relative low salinity water/wastewater.

Keywords

• activated carbon
• selenate
• surface modification
• copper
• adsorption mechanism