Fabrication and Pore Properties of SUS316L Membrane with Double-Layered Pore Structures by Wet Powder Spraying

Abstract

In this study, a SUS316L membrane having double layered pore structures was fabricated, and the pore characteristics were analyzed after coating with a spherical powder and a flake-shaped powder on a disk-shaped SUS316L support using a wet powder spraying process. The thickness of the coated layer was checked using an optical microscope, and air permeability was measured using a capillary flow porometer. When the coating amount was similar, the fine porous layer prepared using flake powder was thicker and showed higher porosity. In the case of a similar thickness, the case of using flake powder was half of the amount of spherical powder used. Therefore, it was confirmed that it is possible to manufacture a metal membrane having a high filter efficiency even with a small coating amount when using the flake powder.