Some studies on the wear resistance of artificial teeth in presence of amorphous SiO2 and TiO2 fillers Estudos da resistência ao desgaste de dente artificial em presença de fillers amorfos SiO2 e TiO2

Abstract

A set of composite materials were developed by blending polymethyl methacrylate (PMMA) with different amounts of micro-fine amorphous silica and titanium dioxide for application as artificial teeth. Wear resistances of these composites were measured with the help of a modified pin-on-disc tribometer and compared with commercial artificial teeth sample in the presence of artificial saliva. It has been observed that under the similar biological condition the powder fillers improved the wear resistances of the artificial teeth as compared to the commercial one under identical condition.Materiais compósitos foram desenvolvidos pela mistura de polimetil metacrilato([PMM)] com diferentes quantidades de sílica amorfa e dióxido de titânio micro-finos para aplicação como dentes artificiais. A resistência ao desgaste desses compostos foi medida com a ajuda de um tribômetro pino-sobre-disco modificado e comparado com a amostra comercial de dentes artificiais na presença de saliva artificial. Foi observado que sob condição biológica similar os compósitos melhoraram a resistência ao desgaste dos dentes artificiais, em comparação com os comerciais nas mesmas condições.

Keywords

• sílica amorfa
• titânia
• dentes artificiais
• PMMA
• resistência ao desgaste
• amorphous silica
• titania
• artificial teeth
• PMMA
• wear resistance