The Wear Behavior of Glass-Ceramic CAD/CAM Blocks against Bovine Enamel

Abstract

The wear of enamel and crown restorative materials often occur by occlusion. The purpose of this study was to evaluate the wear volume between glass-ceramics used for CAD/CAM blocks (lithium disilicate: Initial LiSi block (LIS), IPS e.max CAD (IPS), zirconia-reinforced lithium silicate glass-ceramics: Celtra DUO (DUO), VITA Suprinity (VITS) and feldspar-based glass-ceramics: Vitablocs Mark II (MAK)) and bovine tooth enamel using a two-body wear test, the hardness, three-point bending strength, micro-structure and the element components of glass-ceramics. The data were analyzed using a one-way analysis of variance and Tukey’s multiple comparison test (α = 0.05). IPS and DUO with relatively large size crystal gain had significantly larger abrader wear volumes. Zirconia-reinforced lithium silicate glass-ceramics (DUO, VITS) caused significantly greater wear volume in antagonist enamel. MAK with scale-shape crystals grains produced distinct scratches after wear tests, both in the material itself and in the enamel. A strong correlation between the mechanical properties (hardness, three-point bending strength) and wear volume could not be confirmed. The type of glass-ceramic, size, and shape of the crystal grains affected the wear behavior of the glass-ceramics for CAD/CAM blocks. Therefore, dentists should consider that wear behavior varies with crystal structure, size, and shape in glass-ceramics for CAD/CAM blocks.

Keywords

• two-body wear test
• glass-ceramic
• bovine enamel
• wear behavior
• CAD/CAM blocks