Al/SBA-15 Mesoporous Material: A Study of pH Influence over Aluminum Insertion into the Framework

Abstract

Herein, ordered mesoporous materials like SBA-15 and Al/SBA-15 were prepared using the pH adjustment method. Thus, these materials were developed in different pH of synthesis, from the pH adjustment method using a KCl/HCl solution and varying the Si/Al molar ratio (5, 25, and 75). All the ordered mesoporous materials were characterized by FRX, 27Al NMR, SEM, XRD, N2 adsorption/desorption, and CO2 adsorption. From the applied method, it was possible to obtain SBA-15 and Al/SBA-15 with high mesoscopic ordering based on the XRD patterns, independent of the pH employed. From the chemical composition, the insertion of higher amounts of Al into the synthesis caused a progressive improvement in the structural and textural properties of the ordered mesoporous materials. Thus, the chosen synthesis conditions can lead to different aluminum coordination (tetrahedral and octahedral), which gives these materials a greater potential to be applied. The presence of Al in high amounts provides material with the ability to form micropores. Finally, the proposed method proved to be innovative; low-cost; less aggressive to the environment, with efficient insertion of aluminum in the framework of SBA-15 mesoporous material; and practical, based on only one step.

Keywords

• Al/SBA-15
• hydrothermal synthesis
• pH adjustment
• on-step synthesis