Microstructural and Tensile Property Differences between Ni-16Mo and ODS alloys Fabricated by the Powder Metallurgy Processes

Abstract

Ni-16Mo and ODS alloys were fabricated by the powder metallurgical processes, and their microstructures and tensile properties were investigated. Ni-16Mo-7Cr and Ni-16Mo-7Cr-0.3Ti-0.35Y2O3 (in wt.%) alloys were prepared by mechanical alloying, uniaxial hot pressing, and heat treatment processes. Microstructural observations of these alloys revealed that the Ti and Y2O3 additions to a Ni-16Mo alloy were significantly effective to refine the grain size and form nano-sized Y-Ti-O oxide particles. Consequently, the tensile strengths at room temperature and 700°C were considerably enhanced. This improvement of tensile properties can be mainly attributed to the formation of nano-sized oxide particles, as well as the refined grain size. It is thus concluded that Ni-16Mo alloy with Ti and Y2O3 additions would be very effective in improving the mechanical properties especially at elevated temperatures.

Keywords

• ni-16mo alloy
• oxide dispersion strengthened (ods)
• grain refinement
• nano-oxide particle
• tensile property