Assessing the Feasibility of Fabricating Thermoplastic Laminates from Unidirectional Tapes in Open Mold Environments

Abstract

The automation of the manufacturing processes of thermoplastic composite laminates has become dependent on open mold processes such as automated tape placement (ATP), which couples tape layering with in situ consolidation. The manufacturing parameters of ATP open mold processes, which comprise processing time, consolidation pressure and temperature, affect the bond strength between the plies and the quality of the laminates produced. Therefore, the effect of the manufacturing parameters should be characterized. This work experimentally evaluates the feasibility of fabricating thermoplastic laminates using an open mold process that reasonably models that of ATP. Glass fiber-reinforced polypropylene laminates are fabricated from unidirectional tapes under different consolidation periods, pressures, and temperatures. The bond quality in the produced laminates is assessed by measuring their interlaminar shear strength, which is measured using a short beam standardized shear test in conjunction with digital image correlation. Results show that consolidation can occur at temperatures slightly below the composite tapes’ complete melting temperature, and consolidation times between 7 and 13 min can result in acceptable bond strengths. The results confirmed the feasibility of the process and highlighted its limitations. Analysis of variance and machine learning showed that the effect of process parameters on interlaminar shear strength is nonlinear.

Keywords

• fiber-reinforced polymer composite
• glass fiber polypropylene
• fabrication
• interlaminar shear strength
• adaptive neuro-fuzzy inference system
• analysis of variance