Scanning electron microscopy as a valuable tool to optimize the properties of the polymer/clay nanocomposites

Abstract

AbstractThe current research utilizes a low voltage scanning electron microscopy (LV-SEM) with an electron beam along with low loading energy of lower than 2.2 KeV to minimize damage and specimen surface charging. The NovaSEM, is used as an efficient tool in the current study due to the high resolution information it can gather as images and its high magnification nanometers. Polyamide 12 (PA12), as a polymer matrix, and Cloisite 30B (C30B) nanoclay, as a filling material, were the materials tested in this study. From the results obtained, CBS was found to be a significant and valuable tool for certain complex tasks when studying and analyzing polymer/clay interfaces. CBS in conjunction with beam deceleration in a LV-SEM was used to map the C30B clay distribution on PA12 particles and within PA12-nanoclay nanocomposites manufactured from the latter’s clay distribution particles within the polymer particles’ surfaces. This SEM experimentation has demonstrated that using the clay’s air plasma design preceding the composite preparation resulted in removing the large clay assemblages. The plasma treatment has improved the interfacial adhesion and dispersion in the nanoclay/PA12 composite, resulting in similar maximum stress values which were both higher than the pure PA12. Thus, the mechanical tests exhibited performance enhancement for the resulting composites defined in the present work, and the enhancement of this method can be identified via SEM imaging.

Keywords

• scanning electron microscope
• polymers/clay interfaces
• polymer nanocomposites
• plasma treatment