Dielectric Property and Breakdown Strength Performance of Long-Chain Branched Polypropylene for Metallized Film Capacitors

Abstract

At high temperatures, the insulation performance of polypropylene (PP) decreases, making it challenging to meet the application requirements of metallized film capacitors. In this paper, the dielectric performance of PP is improved by long-chain branching modification and adding different kinds of nucleating agents. The added nucleating agents are organic phosphate nucleating agent (NA-21), sorbitol nucleating agent (DMDBS), rare earth nucleating agent (WBG-Ⅱ) and acylamino nucleating agent (TMB-5). The results show that the long-chain branches promote heterogeneous nucleation and inhibit the motion of molecular chains, thereby enhancing the dielectric properties at high temperatures. Nucleating agents modulate the crystalline morphology of long-chain branched polypropylene (LCBPP), which leads to a decrease in the mean free path of carriers and an increase in trap energy level and trap density. Therefore, the conductivity is reduced and the breakdown strength is improved. Among the added nucleating agents, NA-21 showed a significant improvement in the electrical properties of LCBPP films. At 125 °C, compared with PP, the breakdown strength of the modified film is increased by 26.3%, and the energy density is increased by 66.1%. This method provides a reference for improving the dielectric properties of PP.

Keywords

• long-chain branched polypropylene
• nucleating agent
• crystallization
• high temperature
• dielectric property