Experimental Investigations on the Electrical Conductivity and Complex Dielectric Permittivity of Zn_xMn_1−xFe₂O₄ (x = 0 and 0.4) Ferrites in a Low-Frequency Field

Abstract

Two samples of ZnxMn1−xFe2O4 (x = 0, sample A; and x = 0.4, sample B) were synthesized by the hydrothermal method. From complex impedance measurements in the range 100 Hz–2 MHz and for temperatures T between 30 and 130 °C, the barrier energy between localized states ΔErelax was determined for the first time in these samples. For sample B, a single value of ΔErelax was highlighted (0.221 eV), whilst, for sample A, two values were obtained (0.012 eV and 0.283 eV, below 85 °C and above 85 °C, respectively), associated with two zones of different conductivities. Using the Mott’s VRH model and the CBH model, we determined for the first time both the bandgap energy barrier (Wm) and the hopping (crossover) frequency (ωh), at various temperatures. The results show that, for sample A, Wm has a maximum equal to 0.72 eV at a temperature between 70 and 80 °C, whilst, for sample B, Wm has a minimum equal to 0.28 eV at a temperature of 60 °C, the results being in good agreement with the temperature dependence of the static conductivity σDC(T) of the samples. By evaluating σDC and eliminating the conduction losses, we identified, using a novel approach, a dielectric relaxation phenomenon in the samples, characterized by the activation energy EA,rel. At various temperatures, we determined EA,rel, which ranged from 0.195 eV to 0.77 eV. These results are important, as understanding these electrical properties is crucial to various applications, especially in technologies where temperature variation is significant.

Keywords

• manganese ferrites
• Zn-Mn ferrite
• complex impedance measurements
• electrical conductivity
• complex dielectric permittivity
• VRH and CBH models