Boletín de la Sociedad Española de Cerámica y Vidrio (Aug 2004)
Estudio del Sistema Li<sub>2</sub>SO<sub>4</sub> – Na<sub>2</sub>SO<sub>4</sub>. Diagrama de fases y caracterización del LiNaSO<sub>4</sub>
Abstract
An exhaustive study of the phase diagram of binary system Li2SO4-Na2SO4 is presented. Phase diagram was determined using thermo-X-ray diffraction in powder samples and calorimetry ATD. A new phase with formula Li2-xNaxSO4 has been obtained, with 1 ≤ x ≤ 1.22. The crystal structure of β-LiNaSO4 was determined from single-crystal X-ray diffraction. This study shows that the crystals usually become twinned when the growth is by solution; which explains the poor spontaneous polarization. The Raman dispersion of Li2SO4, Na2SO4 and LiNaSO4 compounds is explained from the structural data. The measurements have been made at different heating and cooling rate.Se presenta un estudio exhaustivo del diagrama de fase del sistema binario Li2SO4-Na2SO4. El diagrama de fases se determinó mediante termo-difractometría de rayos-X en muestras de polvo y calorimetría ATD. Se obtiene una nueva fase de fórmula Li2-xNaxSO4, con 1 ≤ x ≤ 1.22. La estructura cristalina de β-LiNaSO4 se determinó por difracción de rayos-X sobre un monocristal. Este estudio muestra que los cristales usualmente se maclan cuando el crecimiento es por solución, lo cual explica la baja polarización espontánea. Se explica la dispersión Raman de los compuestos Li2SO4, Na2SO4 y LiNaSO4, a partir de los datos estructurales. Las medidas experimentales se han efectuado a diferentes velocidades de calentamiento y enfriamiento.