Study of Coatings Formed on Zirconium Alloy by Plasma Electrolytic Oxidation in Electrolyte with Submicron Yttria Powder Additives

Abstract

Coatings with thickness 40 to 150 μm were formed by plasma electrolytic oxidation (PEO) on the zirconium alloy Zr-1Nb (Zr-1% Nb) in the slurry electrolyte containing 9 g/L Na2SiO3 5H2O, 5 g/L Na(PH2O2) and 6 g/L submicron Y2O3 yttria powder during 60 min under the AC electrical mode at current densities 20; 30 and 40 A/dm2. The surface morphology, structure, composition, and corrosion-protective ability of the formed coatings have been analyzed. At PEO current density 30 A/dm2, a predominantly tetragonal phase of zirconia was formed in coatings. Increasing the PEO current density up to 40 A/dm2 promoted the formation of the coating surface layer containing submicron yttria particles. Electrochemical polarization studies in 0.5% LiOH solution showed that PEO coatings demonstrated high corrosion-protective ability. The dependence of the polarization currents on the PEO current density was found to be inconsequential.

Keywords

• plasma electrolytic oxidation
• zirconium alloy Zr-1Nb
• submicron yttria powder
• PEO coating
• surface morphology
• structure