Evaluation of the effects of temperature and centrifugation time on elimination of uncured resin from 3D-printed dental aligners

Abstract

Abstract The study investigated the effects of temperature and centrifugation time on the efficacy of removing uncured resin from 3D-printed clear aligners. Using a photo-polymerizable polyurethane resin (Tera Harz TC-85, Graphy Inc., Seoul, Korea), aligners were printed and subjected to cleaning processes using isopropyl alcohol (IPA) or centrifugation (g-force 27.95g) at room temperature (RT, 23 °C) and high temperature (HT, 55 °C) for 2, 4, and 6 min. The control group received no treatment (NT). Cleaning efficiency was assessed through rheological analysis, weight measurement, transparency evaluation, SEM imaging, 3D geometry evaluation, stress relaxation, and cell viability tests. Results showed increased temperature and longer centrifugation times significantly reduced aligner viscosity, weight (P < 0.05), and transmittance. IPA-cleaned aligners exhibited significantly lower transparency and rougher surfaces in SEM images. All groups met ISO biocompatibility standards in cytotoxicity tests. The NT group had higher root mean square (RMS) values, indicating greater deviation from the original design. Stress relaxation tests revealed over 95% recovery in all groups after 60 min. The findings suggest that a 2-min HT centrifugation process effectively removes uncured resin without significantly impacting the aligners’ physical and optical properties, making it a clinically viable option.

Keywords

• Centrifugation
• Uncured resin
• Clear aligner
• 3D printing
• Cytocompatibility
• Translucency