Burning characteristics of high density foamed GAP/CL-20 propellants

Abstract

The monolithic foamed propellants with high densities were prepared by casting and two-step foaming processes. Glycidyl azide polymer (GAP) and isocyanate were used as the binder system and 2,4,6,8,10,12-hexanitro-2,4,6,8,10,12-hexaazaisowurtzitane (HNIW, CL-20) was employed as the energetic component. The newly designed formulation containing 60 % CL-20 produced a force constant of 1077 J/g and low flame temperature of 2817 K. Two foamed propellants with densities of 1.32 g/cm3 and 1.53 g/cm3 were fabricated by a confined foaming process and examined by closed bomb tests. The results revealed that porosity significantly affects burning performance. A size effect on combustion behaviors was observed for the foamed propellant with 5.56 % porosity, and a double-hump progressive dynamic vivacity curve was obtained. At last, the 30 mm gun test was carried out to demonstrate the interior ballistic performance, and the muzzle velocity increased by 120 m/s at the same maximum chamber pressure when monolithic propellant was added in the charge.

Keywords

• Monolithic foamed propellants
• Two-step foaming process
• Casting process
• GAP/CL-20