Facile Synthesis of Highly Emissive All-Inorganic Manganese Bromide Compounds with Perovskite-Related Structures for White LEDs
Ping Gao,
Suwen Cheng,
Jiaxin Liu,
Junjie Li,
Yanyan Guo,
Zhengtao Deng,
Tianshi Qin,
Aifei Wang
Affiliations
Ping Gao
Key Laboratory of Flexible Electronics (KLOFE) & Institute of Advanced Materials (IAM), Jiangsu National Synergetic Innovation Center for Advanced Materials (SICAM), Nanjing Tech University (Nanjing Tech), Nanjing 211816, China
Suwen Cheng
Key Laboratory of Flexible Electronics (KLOFE) & Institute of Advanced Materials (IAM), Jiangsu National Synergetic Innovation Center for Advanced Materials (SICAM), Nanjing Tech University (Nanjing Tech), Nanjing 211816, China
Jiaxin Liu
Key Laboratory of Flexible Electronics (KLOFE) & Institute of Advanced Materials (IAM), Jiangsu National Synergetic Innovation Center for Advanced Materials (SICAM), Nanjing Tech University (Nanjing Tech), Nanjing 211816, China
Junjie Li
Key Laboratory of Flexible Electronics (KLOFE) & Institute of Advanced Materials (IAM), Jiangsu National Synergetic Innovation Center for Advanced Materials (SICAM), Nanjing Tech University (Nanjing Tech), Nanjing 211816, China
Yanyan Guo
State Key Laboratory of Analytical Chemistry for Life Science, National Laboratory of Micro-Structures, College of Engineering and Applied Sciences, Nanjing University, Nanjing 210023, China
Zhengtao Deng
State Key Laboratory of Analytical Chemistry for Life Science, National Laboratory of Micro-Structures, College of Engineering and Applied Sciences, Nanjing University, Nanjing 210023, China
Tianshi Qin
Key Laboratory of Flexible Electronics (KLOFE) & Institute of Advanced Materials (IAM), Jiangsu National Synergetic Innovation Center for Advanced Materials (SICAM), Nanjing Tech University (Nanjing Tech), Nanjing 211816, China
Aifei Wang
Key Laboratory of Flexible Electronics (KLOFE) & Institute of Advanced Materials (IAM), Jiangsu National Synergetic Innovation Center for Advanced Materials (SICAM), Nanjing Tech University (Nanjing Tech), Nanjing 211816, China
Lead-free all-inorganic halide materials with different Mn2+-based crystal structures (Cs3MnBr5 and CsMnBr3) were obtained using a convenient synthetic method. Cs3MnBr5 had a bright green emission (522 nm), with a unique single-exponential lifetime (τavg = 236 µs) and a high photoluminescence quantum yield (82 ± 5%). A red emission was observed in the case of the CsMnBr3 structure with a two-exponential fluorescence decay curve, and the lifetime was 1.418 µs (93%) and 18.328 µs (7%), respectively. By a judicious tuning of the synthetic conditions, a mixed phase of Cs3MnBr5/CsMnBr3 was also produced that emitted white light, covering almost the entire visible spectrum. White-light-emitting diodes (WLEDs) with color coordinates (0.4269, 0.4955), a color temperature of (3773 K), and a color rendering index (68) were then fabricated using the as-prepared powder of mixed phases of Cs3MnBr5/CsMnBr3 with a commercial UV LED chip (365 nm).