Electrochemical Behavior of Tantalum Nitride Protective Layers for PEMFC Application

Abstract

Proton Exchange Membrane Fuel Cells (PEMFCs) are promising technology to convert chemical energy from dihydrogen in electrical energy. HT-PEMFCs are working at high temperatures (above 120 °C) and with doped orthophosphoric acid H3PO4 PBI membranes. In such devices, bipolar metallic plates are used to provide reactive gas inside the fuel cell and collect the electrical current. The metallic elements used as bipolar plates, end plates, and interconnectors in acid electrolyte and gaseous fuel cells are severely damaged by a combination of oxidation (due in particular to the use of oxygen, whether pure or contained in the air) and corrosion (due in particular to acid effluents from the electrolyte). This degradation rapidly leads to the loss of the electrical conductivity of the metallic elements and today requires the use of very specific alloys, possibly coated with pure gold. The solution investigated in the present study is the use of a protective coating based on single-phase nitrides obtained by reactive magnetron sputtering or reactive HiPIMS (High-Power Impulse Magnetron Sputtering). The influence of the microstructure on the physical–chemical properties was studied. The electrochemical properties were quantified following two approaches. First, the corrosion current of the developed coatings was measured at room temperature and at higher temperatures using the Linear Sweep Voltammetry (LSV) technique. Then, Electrochemical Impedance Spectroscopy (EIS) measurements were performed to better identify and evaluate their corrosion-resistance performances.

Keywords

• tantalum nitride
• protective layer
• corrosion current
• PEMFC
• fuel cell