Preparation and Lubricating Properties of Polystyrene Composite Microspheres

Abstract

In order to improve the lubrication performance of polystyrene microspheres (PS) as solid lubricant in drilling fluids, elastic graphite–polystyrene composite microspheres (EGR/PS), montmorillonite–elastic graphite–polystyrene composite microspheres (OMMT/EGR/PS), and polytetrafluoroethylene–polystyrene composite microspheres (PTFE/PS) were prepared by suspension polymerization. OMMT/EGR/PS has a rough surface, while the surfaces of the other three composite microspheres are smooth. Among the four kinds of composite microspheres, the largest particle is OMMT/EGR/PS, and the average size is about 400 μm. The smallest particle is PTFE/PS, and the average size is about 49 μm. Compared with pure water, the friction coefficient of PS, EGR/PS, OMMT/EGR/PS and PTFE/PS reduced by 25%, 28%, 48%, and 62%, respectively. The wear tracks of EGR/PS, OMMT/EGR/PS and PTFE/PS are narrower and smoother than those of pure water. When the content of PTFE is 4.0 wt%, the friction coefficient and wear volume of PTFE/PS are 0.213 and 2.45 × 10−4 mm3—74% and 92.4% lower than that of pure water, respectively.

Keywords

• composite microspheres
• lubricating properties
• polystyrene
• PTFE