Synthesis, Acidity and Catalytic of the Rare Earth Ce Loaded on the Composite Pore Zeolite Catalyst for Hydrogenation Cracking

Abstract

Composite molecular sieve Y/SBA-15(C-Y) was prepared by microwave method, while Ce was loaded by ion exchange method to the composite molecular sieves (Ce-Y/SBA-15 (C-X)). Productive-type middle distillate hydrocracking catalyst was prepared from C-X and C-Y loaded. FI-IR, XPS, Pyridine IR, and TG-DTG had been used to characterize the C-X’s and C-Y’s structure and acidity. The results showed that Ce loaded not only had not broken the original structure of C-Y, but also improved silica alumina ratio of C-X, furthermore improved its total acid content. Through polarization and entrainment, Ce increased the skeleton and hydroxyl silicon aluminum hydroxy on electronic probability of migration to the cage, thus enhance the C-X’s B acid strength, make it more suitable for heavy oil processing. As compared with C-Y, the selectivity and yield of middle distillates over C-X was 0.7 % and 1.8 % higher, respectively. C-X have the greatest relief wax oil viscosity index, best once cracking selectivity, and lowest levels of diesel oil solidifying point in the three catalysts.

Keywords

• micro–mesoporous composite materials
• modified molecular sieve
• ce
• synthesis
• characterization
• catalysis