Vertical Etching of Scandium Aluminum Nitride Thin Films Using TMAH Solution

Abstract

A wide bandgap, an enhanced piezoelectric coefficient, and low dielectric permittivity are some of the outstanding properties that have made ScxAl1−xN a promising material in numerous MEMS and optoelectronics applications. One of the substantial challenges of fabricating ScxAl1−xN devices is its difficulty in etching, specifically with higher scandium concentration. In this work, we have developed an experimental approach with high temperature annealing followed by a wet etching process using tetramethyl ammonium hydroxide (TMAH), which maintains etching uniformity across various Sc compositions. The experimental results of etching approximately 730 nm of ScxAl1−xN (x = 0.125, 0.20, 0.40) thin films show that the etch rate decreases with increasing scandium content. Nevertheless, sidewall verticality of 85°~90° (±0.2°) was maintained for all Sc compositions. Based on these experimental outcomes, it is anticipated that this etching procedure will be advantageous in the fabrication of acoustic, photonic, and piezoelectric devices.

Keywords

• scandium doped aluminum nitride (ScAlN)
• wet etching
• tetramethyl ammonium hydroxide (TMAH)
• annealing
• thin films