Experimental Investigation on Wire Electric Erosion Behaviour of Silicon Dioxide Particulate Reinforced Composite

Abstract

The intend of current study was focused on the prediction of material removal rate (MRR) and surface roughness (SR) for the AA7050-SiO2 composite during wire electric erosion or discharge machining (WEDM) process using a brass (Br) wire electrode. Here, stir casting process was employed to develop the AA7050 matrix composite with inclusion of 10wt.% SiO2 particle reinforcement. The multi-objective optimization method of Technique for order preference by similarity to ideal solution (TOPSIS) approach has been applied to find out the optimal setting of input machining parameters such as peak current (Ip), pulse-on time (Ton) and pulse-off time (Toff). Furthermore, the significant effects of parameters were identified by analysis of variance (ANOVA). Taguchi L9 (33) orthogonal design has been formulated to perform the experimental work. TOP SIS results stated that the optimal setting of Ip at 30 amps, Ton of 130 μs and Toff of 55 μs provide the better MRR with lesser SR. The ANOVA results noticed that Ip has the prime noteworthy parameter over the adopted responses having a contribution of 45.67%, followed by Ton (32.34%) and Toff (12.26%), respectively. The confirmation test was carried out by the optimal parameters setting to verify the predicted results. Finally, the scanning electron microscopy (SEM) test was carried out for the machined surface of the composite specimen and it was reveals that the formation of craters and recast layer thickness in the machined surfaces.

Keywords

• aa7050
• sio2
• stir casting
• wedm
• surface roughness
• topsis
• anova