The effect of acidity on the physicochemical properties of two hydraulic calcium silicate-based cements and two calcium phosphate silicate-based cements

Abstract

Abstract Background Bioceramic cements have been widely used in endodontic treatment. This study aimed to compare the microhardness, elastic modulus, internal microstructure and chemical compositions of Biodentine, WMTA, ERRM Putty, iRoot FS and IRM after exposure to PBS, butyric acid, and butyric acid followed by PBS. Methods Specimens of each material were prepared and randomly divided into 5 subgroups (n = 5): subgroup A: PBS (pH = 7.4) for 4 days, subgroup B: PBS (pH = 7.4) for 14 days, subgroup C: butyric acid (pH = 5.4) for 4 days, subgroup D: butyric acid (pH = 5.4) for 14 days, subgroup E: butyric acid for 4 days followed by 10 days in contact with PBS. The surface microhardness, elastic modulus, internal morphologic and chemical compositions of specimens were analyzed. Results The microhardness and elastic modulus values of all materials were significantly higher in the presence of PBS compared to exposure to butyric acid, with the same setting time (P 0.05). Biodentine showed significantly higher microhardness and elastic modulus values than other materials, while IRM displayed the lowest (P < 0.01). Conclusion Biodentine seems the most suitable bioceramic cements when applied to an infected area with acidic pH. Further storage at neutral pH, e.g. PBS reverses the adverse effects on bioceramic cements caused by a low pH environment.

Keywords

• Butyric acid
• Calcium phosphate silicate-based cements
• Calcium silicate-based cements
• Phosphate-buffered saline
• Physicochemical properties