Recovery of Chromium from Slags Leachates by Electrocoagulation and Solid Product Characterization

Abstract

Slags produced in the steelmaking industry could be a source of chromium. Slags contain, depending on different types of slags, between 2 to 5 wt.% of Cr. Roasting of slag with NaOH, followed by subsequent leaching can produce leachates which can be efficiently processed using electrocoagulation (EC). This paper provides results from the EC process optimization for Cr(VI) solutions with initial concentration 1000 mg/L of Cr(VI). Influence of pH, current intensity and NaCl concentration on the efficiency of chromium recovery, energy consumption as well as solid product composition is discussed in detail. Optimum of pH = 6 was chosen for EC processing of Cr leachates as well as current intensities of 0.1–0.5 A because of the higher Cr/Fe ratio in solid product compared to higher current intensities. Results of EC processing of four real leachates of electric arc furnace carbon steel slag (EAFC), electric arc furnace stainless steel slag (EAFS), low carbon ferrochrome slag (LC FeCr) and high carbon ferrochrome slag (HC FeCr) were evaluated. Comparison of the results of four real leachate samples is presented. Obtained final solid product was identified as (Fe0.6 Cr0.4)2O3 and with up to 20% of Cr could be used as source of chromium in the ferrochrome production.

Keywords

• chromium
• electrocoagulation
• metal recovery
• secondary raw materials
• leaching
• slag