Novel application of sodium manganese oxide in removing acidic gases in ambient conditions

Abstract

Abstract In this study, we have demonstrated the application of sodium manganese oxide for the chemisorption of toxic acidic gases at room temperature. The fabricated alkali ceramic has Na0.4MnO2, Na2Mn3O7, and NaxMnO2 phases with a surface area of 2.6 m2 g–1. Na-Mn oxide was studied for oxidation of H2S, SO2, and NO2 gases in the concentration range of 100–500 ppm. The material exhibited a high uptake capacity of 7.13, 0.75, and 0.53 mmol g–1 for H2S, SO2, and NO2 in wet conditions, respectively. The material was reusable when regenerated simply by soaking the spent oxide in a NaOH-H2O2 solution. While the H2S chemisorption process was accompanied by sulfide, sulfur, and sulfate formation, the SO2 chemisorption process yielded only sulfate ions. The NO2 chemisorption process was accomplished by its conversion to nitrite and nitrate ions. Thus, the present work is one of the first reports on alkali ceramic utilization for room-temperature mineralization of acidic gases.