Improvement of magnetic hysteresis loss, corrosion resistance and compressive strength through spark plasma sintering magnetocaloric LaFe11.65Si1.35/Cu core-shell powders

Abstract

LaFe11.65Si1.35/Cu core-shell powders were achieved by self-designed magnetron sputtering system, which presents a better solidification during spark plasma sintering in comparison to the naked LaFe11.65Si1.35 powders. Much higher compressive strength, lower corrosion current density and magnetic hysteresis losses are achieved for the sintered sample of LaFe11.65Si1.35/Cu core-shell powders without significant decrease of the magnetic entropy change. The compressive strength, corrosion current density and maximum magnetic hysteresis losses are 105.6 MPa/16.8 MPa, 1.08 × 10−3A/cm2/3.03 × 10−3 A/cm2 and 1.33 J/kg/2.71 J/kg, respectively for the sintered samples of core-shell structured/naked powders. The technique of fabricating the core-shell structured powders demonstrated here is also applicable for other types of functional powders.