Effect of different polishing systems on the surface roughness of full-contour zirconia

Abstract

Background: Adjustment of any premature occlusal contact of any zirconia restoration requires its polishing or glazing in order to restore the smoothness of the restoration. The objective of this in vitro study was to evaluate the effects of different polishing systems and glazing on the surface roughness of full-contour zirconia. Material and methods: Forty disks (diameter: 8 mm, thickness: 6.4 mm) were prepared from pre-sintered full-contoured zirconia block; they were colored and sintered in a high-temperature furnace at 1500˚C for 8 hours. The specimens were then leveled and finished using grinding and polishing machine and adjusted using diamond disk. The specimens were then randomly divided into four groups (n=10), group I involves samples that were polished using (karat diamond polishing set, Vita zahnfabrik, Germany), group II involves samples that were polished with (zirconia polishing kit, SMEdent, Shanghai, China), group III involves samples that were polished with (OptraFine® diamond polishing system, Ivoclar Vivadent, Germany), while group IV involves samples that were glazed using glazing medium (VITA Akzent Glaze AKZ 25, Vita zahnfabrik, Germany). Surface roughness values (Ra) (in µm) of all the specimens were recorded at each stage of surface treatment of zirconia disks (leveling and finishing, adjustment of the samples and polishing / glazing) using surface roughness tester. Statistical analysis was carried out using one-way ANOVA and LSD tests. Results: The results showed that the glazing group recorded the lowest surface roughness mean value, followed by (OptraFine® polishing system), then (zirconia polishing kit) and finally (karat polishing set) which showed the highest mean of surface roughness. For all groups, there was a statistically very high significant difference of (Ra) value before and after adjustment of the samples. Moreover, there was a statistically very high significant difference in (Ra) value when comparing the adjusted samples with the polished and glazed ones. Karat polishing set group showed a statistically highly significant difference with zirconia polishing kit group (P