Facile Fabrication of Co-Doped Porous Carbon from Coal Hydrogasification Semi-Coke for Efficient Microwave Absorption

Abstract

A Co-doped porous carbon was successfully fabricated by a facile carbonizing procedure using coal hydrogasification semi-coke (SC) as the carbon and cobalt nitrate as the magnetic precursors, respectively. The mass ratio of the precursors was changed to regulate the microwave absorption (MA) capabilities. The favorable MA capabilities are a result of a synergistic interaction be-tween the dielectric loss from the carbon framework, the magnetic loss from nano-sized Co particles, and multiple scattering from the residual pores. At a thickness of 4.0 mm, the Co/C composite showed the lowest reflection loss of −33.45 dB when the initial mass ratio of cobalt nitrate and SC was 1:1. The effective absorbing bandwidth (EAB) could achieve 3.5 GHz at 2 mm thickness. This work not only opens up a new avenue for the facile fabrication of dielectric and magnetic loss combinations and their structural design, but it also creates a new route for the high value-added exploitation of SC.

Keywords

• Co/C composites
• microwave absorption
• dielectric loss
• magnetic loss