An Effective Strengthening Strategy of Nano Carbide Precipitation and Cellular Microstructure Refinement in a Superalloy Fabricated by Selective Laser Melting Process
Kai-Chun Chang,
Meng-Yun Lee,
Tzu-Hou Hsu,
Yao-Jen Chang,
Kai-Chi Lo,
Hyoung Seop Kim,
Kuo-Kuang Jen,
An-Chou Yeh
Affiliations
Kai-Chun Chang
Department of Materials Science and Engineering, National Tsing Hua University, 101, Sec. 2, Kuang-Fu Road, Hsinchu 30013, Taiwan
Meng-Yun Lee
Department of Materials Science and Engineering, National Tsing Hua University, 101, Sec. 2, Kuang-Fu Road, Hsinchu 30013, Taiwan
Tzu-Hou Hsu
Department of Materials Science and Engineering, National Tsing Hua University, 101, Sec. 2, Kuang-Fu Road, Hsinchu 30013, Taiwan
Yao-Jen Chang
Department of Materials Science and Engineering, National Tsing Hua University, 101, Sec. 2, Kuang-Fu Road, Hsinchu 30013, Taiwan
Kai-Chi Lo
Department of Materials Science and Engineering, National Tsing Hua University, 101, Sec. 2, Kuang-Fu Road, Hsinchu 30013, Taiwan
Hyoung Seop Kim
Department of Materials Science and Engineering, Pohang University of Science and Technology (POSTECH), Pohang 37673, Korea
Kuo-Kuang Jen
Missile and Rocket System Research Division, National Chung-Shan Institute of Science and Technology, Taoyuan 325, Taiwan
An-Chou Yeh
Department of Materials Science and Engineering, National Tsing Hua University, 101, Sec. 2, Kuang-Fu Road, Hsinchu 30013, Taiwan
An effective strategy to strengthen a superalloy processed by selective laser melting (SLM) is proposed. The aim is to increase the yield strength of Inconel 718 fabricated by SLM to beyond 1400 MPa, which has never been achieved before. In this study, various NbC additions (0.0%, 0.5%, 1.0%, and 5.0% by weight) were added in the powder bed of Inconel 718, and two types of post-SLM heat treatments were investigated, i.e., solution heat treated plus aging (STA) and direct aging (DA). With NbC addition, smaller depth of melt pool and finer dendritic cells were obtained. Both STA and DA promoted the precipitations of γ′ and γ″. STA eliminated the cellular dendrites and induced grain growth while DA retained the as-built cellular dendrites, grain size, and nano-carbide from NbC addition, rendering a significant 326.2 MPa increase in yield strength. In this work, 0.5% NbC addition exhibited a record-high yield strength of 1461 MPa and ultimate tensile strength of 1575 MPa for Inconel 718 processed by laser manufacturing process according to literature data to-date.