Influence of the ultra-fine fly ash dosages on the mechanical properties of the sulfoaluminate cement-based high water backfilling material

Abstract

Abstract To reduce the filling cost of high-water backfilling material (HWBM) in mining backfill and improve the recycling utilization of the industrial waste such as the coal fly ash. The ultra-fine fly ash (UFA) was added to the HWBM as a partial replacement in this work. Therefore, a series of experiments were performed to investigate the effect of UFA on the mechanical properties of the HWBM at the different curing conditions, then the hydration mechanism of the HWBM blended with UFA was analyzed by XRD and SEM method. The result indicates that the strength of the HWBM decreased with the increasing of UFA dosages, but the addition of UFA can improve the residual strength of the initial HWBM. Additionally, when the HWBM was cured at the laboratory air condition, its carbonation process was restrained obviously as the UFA dosages were less than 15% at the ages of 28 days, which indicates the UFA can improve the weathering resistance of the HWBM with the curing ages increasing effectively. The XRD and SEM results also shows that the degree of crystallinity of the HWBM increased when UFA dosages were less than 15% effectively, while there were few obvious changes on types of hydration products. It indicates that the main affects of UFA on the performance of HWBM is filler and dilution, which reduced the contact area between hydration products of HWBM and CO2 in the air, further improved the carbonation resistance of HWBM.