Stability of Nanocrystalline Spark Plasma Sintered 3Y-TZP

Abstract

Spark plasma sintered 3Y-TZP has been investigated with respect to hydrothermal ageing and grinding. The sintering was performed between the temperatures of 1,100 and 1,600 °C for a soaking time of 5 minutes and the resulting materials were obtained with grain sizes between 65 to 800 nm and relative densities between 88.5 to 98.8%. Experiments on hydrothermal ageing in water vapour at 131 °C, 2 bars during 60 hours shows that phase stability is retained, elastic modulus and hardness of near surface region measured by nanoindentation does not change in fine grain (<200 nm) materials, in spite of porosity. In ground specimens, very small amount of transformation was found for all grain sizes studied.

Keywords

• 3Y-TZP
• grain size
• degradation
• phase transformation