Microstructural Influence on Mechanical Properties of a Lightweight Ultrahigh Strength Fe-18Mn-10Al-0.9C-5Ni (wt%) Steel

Abstract

This study evaluates the role of thermomechanical processing and heat treatment on the microstructure and mechanical properties of a hot rolled, annealed, and aged Fe-18Mn-10Al-0.9C-5Ni (wt%) steel. The steel exhibited rapid age hardening kinetics when aged in the temperature range of 500–600 °C for up to 50 h, which has been shown in other work to be the result of B2 ordering in the ferrite and κ-carbide precipitation within the austenite matrix. The ultimate tensile strength increased from 1120 MPa in the annealed condition to 1230 MPa after 2 h of aging at 570 °C. Charpy V-notch toughness was evaluated at −40 °C in sub-sized specimens with a maximum in the annealed and quenched condition of 28.5 J in the L-T orientation.

Keywords

• lightweight steel
• age hardening
• Fe-Mn-Al-C
• kappa carbide
• B2
• NiAl