Preparation of NiCr/YSZ two-layered burn-resistant coating on γ-TiAl alloys based on plasma surface metallurgy and ion plating methods

Wei D.-B.; Li M.-F.; Zhou X.; Li F.-K.; Li S.-Q.; Zhang P.-Z.

doi:10.2298/JMMB200902005W

Journal of Mining and Metallurgy. Section B: Metallurgy (Jan 2021)

Preparation of NiCr/YSZ two-layered burn-resistant coating on γ-TiAl alloys based on plasma surface metallurgy and ion plating methods

Wei D.-B.,
Li M.-F.,
Zhou X.,
Li F.-K.,
Li S.-Q.,
Zhang P.-Z.

Affiliations

Wei D.-B.: College of Materials Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing, China + Materials Preparation and Protection for Harsh Environment Key Laboratory of Ministry of Industry and Information Technology, Nanjing, China
Li M.-F.: College of Materials Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing, China + Materials Preparation and Protection for Harsh Environment Key Laboratory of Ministry of Industry and Information Technology, Nanjing, China
Zhou X.: College of Materials Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing, China + Materials Preparation and Protection for Harsh Environment Key Laboratory of Ministry of Industry and Information Technology, Nanjing, China
Li F.-K.: College of Materials Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing, China + Materials Preparation and Protection for Harsh Environment Key Laboratory of Ministry of Industry and Information Technology, Nanjing, China
Li S.-Q.: College of Materials Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing, China + Materials Preparation and Protection for Harsh Environment Key Laboratory of Ministry of Industry and Information Technology, Nanjing, China
Zhang P.-Z.: College of Materials Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing, China + Materials Preparation and Protection for Harsh Environment Key Laboratory of Ministry of Industry and Information Technology, Nanjing, China

DOI: https://doi.org/10.2298/JMMB200902005W
Journal volume & issue: Vol. 57, no. 1
pp. 83 – 96

Abstract

Read online

The NiCr/YSZ coating was fabricated on γ-TiAl alloy by double glow plasma surface metallurgy technology and multi-arc ion plating technology. The microstructure, microhardness, bonding strength, and burn resistance of NiCr/YSZ coating were studied in detail. The results showed that the NiCr/YSZ coating was dense and homogeneous, including a duplex structure of top YSZ ceramic coating and underlying Ni-Cr bond coating. The average microhardness of NiCr/YSZ coating was raised by a factor of about 2 compared to the γ-TiAl substrate. The thermal shock test indicated that the composite structure had superior bonding strength and the defects such as metal droplets on the ceramic coating were the source of cracks. The high-energy laser beam destroyed the surface of γ-TiAl alloy, forming protruding combustion products in ablation zone and splashing residues around ablation zone. When coated by NiCr/YSZ coating, the combustion process was delayed through isolating and dissipating heat. The ablation range was controlled and the ablation damage was reduced at the same irradiation power. The NiCr/YSZ coating preliminarily realized to improve the burn resistance of γ- TiAl alloy.

Published in Journal of Mining and Metallurgy. Section B: Metallurgy

ISSN: 1450-5339 (Print); 2217-7175 (Online)
Publisher: Technical Faculty, Bor
Country of publisher: Serbia
LCC subjects: Technology: Mining engineering. Metallurgy
Website: http://www.doiserbia.nb.rs/journal.aspx?issn=1450-5339

About the journal

Abstract

Keywords