China Foundry (Nov 2008)
Influence of titanium content on wear resistance of electrolytic low-titanium eutectic Al-Si piston alloys
Abstract
The wear resistance of six kinds of the electrolytic low-titanium eutectic Al-Si piston alloys with various Ti content ranging from 0.00wt.% to 0.21wt.% has been studied. A new method of adding Ti is adopted in the electrolytic low-titanium aluminum alloy ingots. The electrolytic low-titanium eutectic Al-Si piston alloys are produced by remelting the electrolytic low-titanium aluminum alloy, crystal silicon, pure magnesium, Al-50%Cu and Al-10%Mn master alloy. The wear experiments are conducted using MM200 wear testing machine under lubricating condition. The results indicate that the better wear resistance and the less weight loss are achieved in the study for the eutectic Al-Si piston alloys with 0.08wt.%–0.12wt.% Ti content. The highest ultimate tensile strength of 135.94 MPa at 300℃ and HV141.70 hardness of the alloys are obtained at 0.12wt.% and 0.08wt.% Ti content, respectively. The wear mechanism of the eutectic Al-Si piston alloys under lubricating condition is abrasive wear.