Optimization of conditions for growth of vanadium dioxide thin films on silicon by pulsed-laser deposition

Abstract

We systematically examined the effects of the substrate temperature (TS) and the oxygen pressure (PO2) on the structural and optical properties polycrystalline V O2 films grown directly on Si(100) substrates by pulsed-laser deposition. A rutile-type V O2 phase was formed at a TS ≥ 450 °C at PO2 values ranging from 5 to 20 mTorr, whereas other structures of vanadium oxides were stabilized at lower temperatures or higher oxygen pressures. The surface roughness of the V O2 films significantly increased at growth temperatures of 550 °C or more due to agglomeration of V O2 on the surface of the silicon substrate. An apparent change in the refractive index across the metal–insulator transition (MIT) temperature was observed in V O2 films grown at a TS of 450 °C or more. The difference in the refractive index at a wavelength of 1550 nm above and below the MIT temperature was influenced by both the TS and PO2, and was maximal for a V O2 film grown at 450 °C under 20 mTorr. Based on the results, we derived the PO2 versus 1/TS phase diagram for the films of vanadium oxides, which will provide a guide to optimizing the conditions for growth of V O2 films on silicon platforms.