Effect of surface tension and drying time on inkjet-printed PEDOT:PSS for ITO-free OLED devices

Abstract

Highly conductive PEDOT:PSS is one of the most promising materials for indium tin oxide (ITO) substitution in printed electronics. Here, we report the development and optimisation of two PEDOT:PSS ink formulations for the fabrication of inkjet-printed transparent conductive layers. Starting from aqueous commercial solutions, co-solvents and a non-ionic surfactant were employed to modify the surface tension, improve the wetting capability of the ink, and obtain uniform and homogeneous thin films. In particular, the quantities of ethanol and surfactant were systematically adjusted to determine the optimal conditions for inkjet printing. The results demonstrate that a surface tension value between 28 and 40 mN/m and approximately 40 vol.% of a low-boiling-point co-solvent are fundamental to ensure the proper wetting of the glass substrate and a quick-drying process that confers uniformity to the printed thin film. The printed PEDOT:PSS thin films show good morphological, optical, and electrical properties that are similar to those observed for the corresponding spin-coated layers. The organic light-emitting diodes (OLEDs) fabricated with the inkjet-printed PEDOT:PSS electrodes showed a maximum quantum efficiency of 5.5% and a maximum current efficiency of 15 cd/A, which is comparable to spin-coated reference devices. Our study demonstrates the great potential of polymeric electrodes for the fabrication of high-efficiency printed OLED devices that are compatible with flexible and stretchable substrates.

Keywords

• PEDOT:PSS
• Surface tension
• Co-solvent
• Inkjet printing
• Organic light-emitting diodes
• ITO-Free